Miwa, Yukio; Tsukada, Takashi
Proceedings of 8th Japan-China Symposium on Materials for Advanced Energy Systems and Fission & Fusion Engineering, p.161 - 168, 2004/10
Irradiation assisted stress corrosion cracking (IASCC) is one of the environmental degradation problems of in-core structural materials for light water reactors. The effects of irradiation and water temperatures on the IASCC were studied using type 316(LN) stainless steels irradiated at 333-673 K to 1.1-16 dpa. IASCC did not occur at 513 K in oxygenated water for specimens irradiated below 573 K to 1.1-16 dpa, but IASCC occurred above 533 K in oxygenated water for all specimens. The irradiation temperature had a strong influence on IASCC susceptibility at 513 K in oxygenated water, so that the irradiation temperature dependence was compared with the temperature dependence of other radiation-induced phenomena.